The creep strengths for an annealed Ni-33Fe-25Cr alloy, UNS N08120 (HAYNES® HR-120® alloy) are presented from 593°C to 1204°C at every 56°C for lives up to 30,000 hours. The creep data are used as a basis for converting the power law method (log stress versus log time at a defined temperature) to the usefulness of the Larson-Miller method for design creep analysis. A new empirical relationship was developed between stress, temperature and creep rupture life. Power Law equations were generated at each temperature using linear regression of the transformed data to obtain the best-fit constants. The constants were then plotted and a best-fit polynomial of the constants as a function of temperature was determined. The polynomial then replaced the constants in the original power law equation to obtain a single expression of stress as a function of time and temperature. Using this new Modified Power Law (MPL) equation, interpolation or extrapolation to obtain stress becomes possible for any temperature and time.

F. R.
, and
, “
A Time-Temperature Relationship for Rupture and Creep Stresses
,” Trans. ASME, July, pp. 765–775.
Conway, J. B., 1969, Stress-Rupture Parameters: Origin, Calculations and Use, Gordon & Breach, New York, pp. 43–47.
Sjodahl, L. H., 1978, “A Comprehensive Method of Rupture Data Analysis With Simplified Models,” Characterization of Materials for Service at Elevated Temperatures, MPC-7, ASME/CSME Montreal Pressure Vessel & Piping Conference, ASME, New York.
Katcher, M., 1998, “Creep Analysis of Solid Solution Strengthened Nickel Alloys,” Fatigue, Environmental Factors, and New Materials, 374, ASME, New York.
Dieter, G. E., 1986, Mechanical Metallurgy, McGraw Hill, pp. 483–487.
Srivastava, S. K., Lai, G. Y., and Warner, T. L., 1995, “Creep-Rupture Behavior of an Fe-Ni-Cr-Nb-N Alloy (HR-120 Alloy),” Conference Proceedings of the 2nd Intl. Conf. on Heat Resistant Materials, September 11–14, Gatlinburg, TN.
Sims, C. T., Stoloff, N. S., and Hagel, W. C., 1987, Superalloys II, John Wiley, New York, p. 87.
Tackett, J. W., 1971, “The Creep Rupture Properties of Haynes Alloy No. 188,” Stellite Division Cabot Corporation, Kokomo, IN (now Haynes International).
You do not currently have access to this content.