Leak-before-break (LBB) is a term that has been used for decades in reference to a methodology that means that a leak will be discovered prior to a fracture occurring in service. LBB has been applied to missile casings, gas and oil pipelines, pressure vessels, nuclear piping, etc. LBB also has several technical definitions. For instance, LBB can occur for an axial flaw in a pipe where the penetration of the wall thickness will result in a stable axial through-wall crack. This is LBB under load-controlled conditions. LBB could also occur for a circumferential crack in a pipe with high thermal expansion stresses. This might be LBB under compliant displacement-controlled conditions. Finally, LBB might occur when the flaw is stable under normal operating conditions and remains stable when there is a sudden dynamic event (i.e., seismic loading). This might be a time-dependant inertial LBB analysis. These analyses are deterministic, and could be extended to probabilistic evaluations as well. This paper describes some of the technical LBB approaches, applications, and significance of the methodology used in the applications. [S0094-9930(00)01603-6]

Issue Section:
Technical Papers
Keywords:
pressure vessels, fracture, cracks, failure (mechanical)
Topics:
Displacement, Fracture (Materials), Pipes, Stress, Leak-before-break
1.
Irwin, G. R., 1963, “Fracture of Pressure Vessels,” Materials for Missiles and Spacecraft, pp. 204–229, McGraw-Hill, New York, NY.
2.
Kobayashi
,
A. S.
,
Zii
,
M.
, and
Hall
,
L. R.
,
1965
, “
Approximate Stress Intensity Factor for an Embedded Elliptical Crack Near Two Parallel Free Surfaces
,”
Int. J. Frac. Mech.
,
1
, pp.
81
–
95
.
3.
Folias, E. S., 1964, “The Stresses in a Cylindrical Shell Containing an Axial Crack,” ARL 64-174, Aerospace Research Laboratories, Oct.
4.
Pellini, W. S., 1969, Evolution of Engineering Principles for Fracture-Safe Design of Steel Structures, Naval Research Laboratory Report NRL 6957, September 23.
5.
Milne, I., et al., 1986, “Assessment of the Integrity of Structures Containing Defects,” CEGB Report R/H/R6-Revision 3.
6.
Kiefner, J. F., et al., 1973, “Failure Stress Levels of Flaws in Pressurized Cylinders,” Progress in Flaw Growth and Fracture Toughness Testing, ASTM STP 536, American Society for Testing and Materials, pp. 461–481.
7.
ASME Boiler and Pressure Vessel Code, 1995, Section XI, Rules for In-service Inspection of Nuclear Power Plant Components, Article IWB-3600, July.
8.
American National Standards Institute (ANSI)/American Society of Mechanical Engineers (ASME), 1984, B31G “Manual for Determining the Remaining Strength of Corroded Pipelines.”
9.
Kussmaul, K., et al., 1985, “Pha¨nomenologische Beha¨lterberstversuche—Phase I,” BMFT Report BMFT-TB-1500 279, by MPA-Stuttgart, July.
10.
Bryan, R. H., Bolt, S. E., Merkle, J. G., and Whitman, 1982, “Quick-Look Report on Test of Intermediate Vessel V-8a—Tearing Behavior of Lower Upper,” ORNL/SST-4, Oakridge National Laboratory, Aug.
11.
Proc. IAEA, 1983, Theoretical and Experimental Work on LMFBR Steam Generator Integrity and Reliability with a Particular Reference to Leak Development and Detection, IAEA Document IWGFR/50, Nov.
12.
Moan
,
G. D.
,
Coleman
,
C. E.
,
Price
,
E. G.
,
Rodgers
,
D. K.
, and
Sagat
,
S.
,
1990
, “
Leak-Before-Break in the Pressure Tubes of CANDU Reactors
,”
Int. J. Pressure Vessels Piping
,
43
, pp.
1
–
21
.
13.
Pierce, W., 1970, “Effects of Surface and Through Cracks on Failure of Pressurized Thin-Walled Cylinders of 2014-T6 Aluminum,” NASA Report TN D6099, Nov.
14.
Eiber, R. J., Maxey, W. A., and Duffy, A. R., 1971, “Fracture Investigation of Pipe for LNG Service,” Battelle report to A.G.A. on Project PR-3-42, Dec.
15.
Rana
,
M. D.
,
1987
, “
Experimental Verification of Fracture Toughness Requirements for Leak-Before-Break Performance for 155–175 ksi Strength Level Gas Cylinders
,”
ASME J. Pressure Vessel Technol.
,
109
, Nov., pp.
435
–
439
.
16.
Wilkowski
,
G. M.
, and
Eiber
,
R. J.
,
1981
, “
Evaluation of Tensile Failure of Girth Weld Repair Grooves in Pipe Subjected to Offshore Laying Stresses
,”
ASME J. Energy Resour. Technol.
,
103
, Mar., pp.
48
–
57
.
17.
Solicitation for Public Comment on Standard Review Plan 3.6.3, 1987, “Leak-Before-Break Evaluation Procedures,” Federal Register, Vol. 52, No. 167, August 28.
18.
Wilkowski
,
G. M.
,
Zahoor
,
A.
, and
Kanninen
,
M. F.
,
1981
, “
A Plastic Fracture Mechanics Prediction of Fracture Instability in a Circumferentially Cracked Pipe in Bending—Part II: Experimental Verification on a Type 304 Stainless Steel Pipe
,”
ASME J. Pressure Vessel Technol.
,
103
, Nov., pp.
359
–
365
.
19.
Wilkowski, G. M., and Kramer, G., 1989, “An Energy Balance Approach to Estimate the Initiation and Arrest of Ductile Fracture Instability in Circumferentially Cracked Pipe,” ASME PVP-Vol. 167, July, pp. 103–114.
20.
Olson, R., Wolterman, R., Scott, P., Krishnaswamy, P., and Wilkowski, G., 1994, “The Next Generation Methodology for Cracked Pipe System Subjected to Dynamic Loads,” ASME PVP-Vol. 275-1, June, pp. 159–172.
21.
Hopper, A. T., Wilkowski, G. M., Scott, P. M., Olson, R. O., Rudland, D., Kilinski, T., Mohan, R., Ghadiali, N., and Paul, D., 1997, “The Second International Piping Integrity Research Group (IPIRG-2) Program—Final Report,” NUREG/CR-6452, Feb.
22.
Wilkowski, G. M., Olson, R. J., and Scott, P. M., 1998, “State-of-the-Art Report on Piping Fracture Mechanics,” U.S. Nuclear Regulatory Commission report NUREG/CR-6540, BMI-2196, Feb.
23.
Harris, D. O., Lim, E. Y., and Dedhia, D. D., 1981, “Probability of Pipe Fracture in the Primary Coolant Loop of a PWR Plant,” NUREG/CR-2189, Vol. 5, Aug.
24.
Rahman, S., et al., 1995, “Probabilistic Pipe Fracture Evaluations for Leak-Rate-Detection Applications,” NUREG/CR-6004, Apr.
Copyright © 2000
 by ASME
You do not currently have access to this content.