The principal mechanisms of failure of high temperature components include creep, fatigue, creep-fatigue, and thermal fatigue. In heavy section components, although cracks may initiate and grow by these mechanisms, ultimate failure may occur at low temperatures during startup-shutdown transients. Hence, fracture toughness is also a key consideration. Considerable advances have been made both with respect to crack initiation and crack growth by the above mechanisms. Applying laboratory data to predict component life has often been thwarted by inability to simulate actual stresses, strain cycles, section size effects, environmental effects, and long term degradation effects. This paper will provide a broad perspective on the failure mechanisms and life prediction methods and their significance in the context utility deregulation. [S0094-4289(00)00103-1]

Issue Section:
Technical Papers
Keywords:
power plants, creep, fatigue, creep fracture, thermal stress cracking, fracture toughness, structural engineering, welding, high-temperature effects
Topics:
Creep, Failure, Fracture (Materials), Welded joints, High temperature, Damage, Fracture (Process), Fatigue
1.
Viswanathan, R., 1987, “Damage Mechanisms and Life Assessment of High Temperature Components,” ASM International Metals Park, OH.
2.
Viswanathan, R., and Bernstein, H., 1996, “Some Issues in Creep Fatigue Life Predictions of Fossil Power Plant Components,” ASME PVP, Vol. 335, Service Experience and Design In Pressure Vessels and Piping, W. H. Barnford, ed., Book No. H01063, pp. 99–119.
3.
Viswanathan
,
R.
, and
Jaffe
,
R. I.
,
1983
, “
Toughness of Cr-Mo-V Steels for Steam Turbine Rotors
,”
ASME J. Eng. Mater. Technol.
,
105
, pp.
286
–
294
.
4.
Roberts
,
D. I.
, et al.,
1985
, “
Dissimilar Weld Failure Analysis and Development Program
,”
Final Report
CS-4252, Vols. 1-7, Electric Power Research Institute, Palo Alto, CA.
5.
Roberts
,
D. I.
,
Ryder
,
R. H.
, and
Viswanathan
,
R.
,
1985
, “
Performance of Dissimilar Welds in Service
,”
ASME J. Pressure Vessel Technol.
,
107
, pp.
247
–
254
.
6.
Ellis
,
F. V.
, et al.,
1988
, “
Remaining Life Assessment of Boiler Pressure Parts
,”
Final Report
RP2253-1, Vol. 1-5, Electric Power Research Institute, Palo Alto, CA.
7.
Henry, J. F., et al., “Failure Investigation of Longitudinal Seam Welded Elevated Temperature Header,” Microstructural Science, M. E. Blum et al., eds., 15, ASM International, pp. 150–169.
8.
Hickey, J. J., et al., 1995, “Investigation and Repair of a Failed Seam Welded Reheat Outlet Header,” Proc. of Conf. Welding and Repair Technology for Power Plants, Daytona Beach, Electric Power Research Institute, Palo Alto, CA, May.
9.
Chan, W., McQueen, R. L., Prince, J., and Sidey, D., 1991, “Metallurgical Experience with High Temperature Piping in Ontario Hydro,” ASME PVP, Vol. 21, Service Experience in Operating Plants, ASME, New York.
10.
Wells, C. H., and Viswanathan, R., 1993, “Life Assessment of High Energy Piping,” Technology for the 90s, M. K. Au-Yang et al., eds., ASME Pressure Vessels and Piping Division, New York, pp. 179–216.
11.
Viswanathan, R., and Foulds, J., 1995, “Failure Experience with Seam-Welded Hot Reheat Pipes in the USA,” ASME PVP, Vol. 303, Service Experience, Structural Integrity, Severe Accidents and Erosion in Nuclear and Fossil Plants, S. R. Paterson et al., eds., ASME, New York, pp. 187–207.
12.
Foulds
,
J. R.
,
Viswanathan
,
R.
,
Landrum
,
L.
, and
Walker
,
S. L.
,
1995
, “
Guidelines for the Evaluation of Seam Welded High Energy Piping
,” Report TR-104631, Electric Power Research Institute, Palo Alto, CA.
13.
Ellis, F., and Viswanathan, R., 1998, “Review of Type IV Cracking in Welds,” ASME PVP Conference, July 1998, PVP, Vol.380, Fitness for Service Evaluation in Petroleum and Fossil Plants, pp. 59–76.
14.
Neubauer, B., and Wedel, V., 1983, “Rest Life Estimation of Creeping Components By Means of Replicas,” Advances in Life Prediction Methods, D. A. Woodford and J. R. Whitehead, eds., ASME, New York, p. 307.
15.
Kuwabara, K., Nitta, A., and Kitamura, T., 1985, Advances in Life Prediction, D. A. Woodford and R. Whitehead, eds., ASME, New York, pp. 131–141.
16.
B_oiler L_ife E_valuation and S_imulation S_ystem, BLESS Code and User Manual,
1991
, Report TR-103377, Vol. 4, Electric Power Research Institute, Palo Alto, CA.
Copyright © 2000
 by ASME
You do not currently have access to this content.